Características
1. Cold work tool steel with high dimensional stability at heat treatment.
2. Very high cracking resistance. High machinability, medium thoughness and wear resistance.
Tratamento Térmico
Recozimento
680 to 720°C
Slow controlled cooling in furnace at a rate of 10 to 20°C/hr down to approx. 600°C, further cooling in air. Hardness af ter annealing: Max. 220 HB.
Endurecimento
790 to 820°C
Oil, salt bath (200 to 250°C) up to 20 mm thickness. Holding time after temperature equalization: 15 to 30 minutes. Obtainable hardness: 63 – 65 HRC
Alívio de Tensões
Aprox. 650°C
Resfriamento lento em forno; destinado a aliviar tensões geradas por usinagem extensa ou em peças de geometria complexa. Após aquecimento completo, manter em atmosfera neutra por 1 a 2 horas.
Revenimento
Slow heating to tempering temperature immediately after hardening/time in furnace 1 hour for each 20 mm of work piece thickness, but at least 2 hours/cooling in air.For certain cases we recommend to reduce tempering temperature and increase holdingtime.
Informações básicas. Nº do modelo: Molde de injeção. Processo de fabricação: Moldagem por injeção. Tipo de moldagem: Moldagem única. Certificação: CE, ISO. Personalizado. Forma personalizada conforme seus desenhos. Serviço: OEM.
Informações básicas. Nº do modelo: Molde de injeção. Base do molde: Cavidade única. Material plástico: Ver descrição detalhada. Tipo de processo: Modo de processo único. Aplicação: Automóveis, eletrodomésticos.,
Nome do produto: Base de molde personalizada para moldes plásticos e moldes de fundição sob pressão. Material do molde: 1.2311/P20; 1.2738/718; 1.2083/420/4Cr13/S136; 1.2344/H13; NAK80; 1.1730/C45/S50C/S355, etc. Centro de usinagem CNC: 24 conjuntos.
Seu parceiro confiável em aços para ferramentas na fabricação de moldes.
Direitos Autorais © 2026 Ningbo Ningshing Precision Machinery Group Co., Ltd